Fe45鐵鎳鉻硅硼合金粉末 噴涂噴焊鐵基合金粉廠家

鐵基自熔性合金是鐵碳合金中加入一定量的硼、硅元素制成的，通常應用在常溫500以下耐磨損、耐弱酸腐蝕介質的機械零部件上，僅管鐵基自熔性合金，綜合性能不如鎳、鈷基合金，然而原料來源廣泛，價格便宜，這是其得以普及應用的較大優勢。下面介紹我公司鐵基焊粉，建議用戶在使用前應在120保溫兩小時低溫烘烤后使用。

Iron-base fluxed alloy is produced by adding suitable amount of boron and silicon into iron-carbon alloy, which is usually used on the wearable and weak-acid-medium proofing accessories under 500. Although the performance of iron-base fluxed alloy can not match with that of the nickel or cobalt alloy, it has wide source materials and low prices, which is the great advantage for application. The following iron-base sprayed welding alloy powder should be dried by the customer under 120 for two hours before useing. 　　

型號

規格

特性簡述

主要用途

物理性能

應用工藝

Fe1

-200/ 100

Fe1是奧氏體不銹鋼型加入B、Si元素具有抗磨耐熱、耐用腐蝕和抗熱疲勞等綜合性能。

閥門密封面
熱軋輥

HRC35-40
熔點1250流動性17s/50g
松裝密度4.4g/cm3

等離子棧焊

Fe2

-200/ 100

同上

同上閥門座

HRC38-44
熔點1240同上
同上

等離子棧焊

Fe5

-200/ 100
-106/ 45

Fe5是高鉻鑄鐵型抗磨料磨損性極優，裂紋傾向大。

石油鉆桿接頭,犁鏵耙片等磨粒磨損工件

HRC62-67
熔點1230流動性18s/50g
松裝密度4.5g/cm3

等離子棧焊
氧乙炔一步法噴焊

Fe90

-150/ 53
-106/ 45

Fe90發球半馬氏體鋼，在Icr13不銹鋼中加入B、Si元素和少量Mo具有耐磨、耐腐蝕等良好性能，抗裂性好。

石油鉆桿接頭鉆鋌保護層

HRC50-55
熔點1250流動性18s/50g
松裝密度4.5g/cm3

等離子棧焊

Fe6

-150/ 53
-106/ 45

Fe6是低鉻高Ni加有B、Si元素之Fe基焊粉，其工藝性比ni60粉差，但具有Ni60粉綜合性能，價格便宜。

風機葉片,拔絲滾,
鏟片

HRC58-60
熔點1080流動性17s/50g
松裝密度4.6g/cm3

等離子棧焊
氧乙炔噴焊

Fe45

-150/ 53
-106/ 45

Fe45是加有B、Si元素的高Ni鐵合金粉具有Ni45合金粉性能，工藝性稍差價格便宜。

鐵軌修復

HRC40-46
熔點1070流動性17s/50g
松裝密度4.6g/cm3

等離子棧焊