OK AUTROD NICRMO-3/ERNiCrMo-3
<分類: | ERNiCrMo-3,SFA/AWS A5.14,S Ni 6625 ,EN ISO 18274 | **:For NV1.5Ni up to NV9Ni,Only valid for lot numbers starting with MV,DNV,10003,VdTüV |
Approvals are based on factory location. Please contact ESAB for more information.
?
<Alloy Type: | Alloyed nickel |
夏比V型缺口沖擊性能
<Impact Value | Testing Temperature | Stress Relieved Testing Temp | Stress Relieved Testing Time | As welded130 J20 °C | - | - | 120 J-105 °C | - | - | 110 J-196 °C | - | - | Stress relieved140 J20 °C | 550 °C | 15 hr | 120 J-196 °C | 550 °C | 15 hr | SHT 1175°C 0.5h185 J20 °C | - | - | 170 J-105 °C | - | - | 150 J-196 °C | - | - |
?
Typical Tensile Properties
<Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time | As welded45 %780 MPa | 500 MPa | - | - | As welded 48 %580 MPa | 380 MPa | - | - | Stress relieved40 %796 MPa | 490 MPa | 550 °C | 15 hr | SHT 1175°C 0.5h46 %765 MPa | 375 MPa | - | - | SHT 1175°C 0.5h46 %590 MPa | 270 MPa | - | - |
?
熔敷數據
<安培 | 熔敷率 | 電壓 V | 直徑 | 送絲速度 | 70-190 A1,3-4,8 kg/h | 20-27 V | METRIC_0.8 mm | IMPERIAL_5-18 m/min | 100-200 A2,5-5,5 kg/h | 21-27 V | METRIC_1.0 mm | IMPERIAL_6-13 m/min | 160-280 A3,6-6 kg/h | 24-30 V | METRIC_1.2 mm | IMPERIAL_6-10 m/min | 200-350 A4,3-8,6 kg/h | 25-32 V | METRIC_1.6 mm | IMPERIAL_4-8 m/min | -- | - | METRIC_1.6 mm | - |