上海斯米克S223無硅錫黃銅焊絲這里看

上海斯米克S223無硅錫黃銅焊絲?

Category

類別

Trade

mark

牌號

Chemical composition

主要成份

Characteristics & application

特性和用途

Equivalent to AWS

相當AWS

?

Hardfacing

?

硬

?

面

?

棧

?

焊

S 101

C3 Cr28 Ni4

Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.

HRc48-54，耐磨、耐氣蝕、抗氧化。棧焊鏟斗齒，泵套

?

S 111

C1 Cr29 W5

Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.

HRc38-47，高溫下耐磨、耐蝕。棧焊高溫高壓閥門

ECoCr-A

S 112

C1.5 Cr29 W8

Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.

HRc45-50，高溫下耐磨、耐蝕。棧焊閥門，熱軋孔型

ECoCr-B

S 113

C2.5 Cr30 W17

Co Rem.

HRc55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.

HRc55，高溫下耐磨、耐熱，但抗沖擊性差。棧焊螺旋送料機用

?

S 114

C2.5 Cr30 W12

Co Rem.

HRc53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.

HRc53，高溫下耐磨、耐熱，但抗沖擊較差。棧焊牙輪鉆頭

ECoCr-C

?

Copper

alloys

?

?

銅

?

?

合

?

?

金

S 201

Sn1 Si0.3Mn0.3

Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.

機械性能好，抗裂性好。紫銅氣焊及氬弧焊用

ERCu

S 211

Si3 Mn1

Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.

機械性能好，銅合金氬弧焊及鋼的MIG釬焊用

ERCuSi-Al

S 212

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨性好。銅合金氬弧焊及鋼的棧焊用

ERCuSn-A

S 213

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨性好。銅合金氬弧焊及鋼的棧焊用

ERCuSn-C

S 214

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨、耐蝕。銅合金氬弧焊及鋼的棧焊用

ERCuAl-A1

S 215

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.

耐磨、耐蝕。銅合金氬弧焊及鋼的棧焊用

ERCuAl-A2

S 221

Cu60 Sn1 Si0.3

Zn Rem.

Melting point is about 890. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔點約890。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

?

S 221F

Cu60 Sn1 Si 0.3

Zn Rem.

S221 welding rod coated with flux.

外涂焊劑的S221焊絲

?

S 222

Cu58Sn0.9Si0.1

Fe0.8 Zn Rem.

Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔點約880。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

RBCuZn-C

S 222F

Cu58Sn0.9Si0.1

Fe0.8 Zn Rem.

S222 welding rod coated with flux.

外涂焊劑的S222焊絲

RBCuZn-C

S 223

Cu59 Sn0.6

Zn Rem.

Melting point is about 900. Braze welding of copper, steel and cast iron.

熔點約900。銅、鋼、鑄鐵釬焊用

上海斯米克S223無硅錫黃銅焊絲?

RBCuZn-A

S 224

Cu62 Si0.5

Zn Rem.

Melting point is about 905. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔點約905。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

?

Copper

alloys

銅

?

合

?

金

S 225

Cu48 Ni10

Zn Rem.

Melting point is about 935and high strength. Braze welding of steel, nickel and carbide alloys.

熔點約935。高強度,釬焊鋼、鎳及硬質合金用

RBCuZn-D

S 225F

Cu48 Ni10

Zn Rem.

S225 welding rod coated with flux.

外涂焊劑的S225焊絲

RBCuZn-D

S 226

Cu60 Sn0.3

Si0.2 Zn Rem.

Melting point is about 900. Gas welding of brass, also braze welding of copper, steel and cast iron.

熔點約900。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵

?

S 227

Cu58Sn0.9Ni0.5

Si0.1 Fe0.8

Zn Rem.

Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.

熔點880。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

RBCuZn-B

S 229

Cu55 Ni6 Mn4

Zn余

Melting point is about 920, high strength. Braze welding of steel, nickel and hard carbide.

熔點約920。高強度,釬焊鋼、鎳及硬質合金用

?

Aluminum alloys

?

鋁

?

合

?

金

S 301

Al99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.

塑性好、耐蝕。純鋁氣焊、氬弧焊用

ER1100

S 311

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.

抗裂性好，通用性大。鋁合金氣焊、氬弧焊用。不宜用高鎂合金

ER4043

S 321

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.

良好的耐蝕性、可焊性及塑性。鋁合金氣焊、氬弧焊用

?

S 331

Mg5 Mn0.4

Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.

耐蝕，強度高。鋁合金氬弧焊用

上海斯米克S223無硅錫黃銅焊絲?