OK ARISTOROD 69/ER110S-G
<分類: | G 69 4 M Mn3Ni1CrMo,EN ISO 16834-A,G Mn3Ni1CrMo,EN ISO 16834-A,ER110S-G,SFA/AWS A5.28 | **:ER 110S-G ,ABS,EN 13479,CE,42.039.33,DB,IV Y69MS,DNV,4Y69M,GL,11837,VdTüV,1.2MM,NAKS/HAKC | Approvals are based on factory location. Please contact ESAB for more information.
<Alloy Type: | Low alloyed | 夏比V型缺口沖擊性能<Impact Value | Stress Relieved Testing Temp | Stress Relieved Testing Time | Testing Temperature | EN 80Ar/20CO2? ?Stress relieved130 J620 °C | 15 hr | 20 °C | 60 J620 °C | 15 hr | -20 °C | 60 J620 °C | 15 hr | -30 °C | EN 80Ar/20CO2? ?As welded100 J- | - | 20 °C | 73 J- | - | -40 °C | EN 80Ar/20CO2? ?Stress relieved130 J620 °C | 15 hr | 20 °C | 60 J620 °C | 15 hr | -20 °C | 60 J620 °C | 15 hr | -30 °C | EN 80Ar/20CO2? ?As welded100 J- | - | 20 °C | 73 J- | - | -40 °C | EN 80Ar/20CO2? ?Stress relieved130 J620 °C | 15 hr | 20 °C | 60 J620 °C | 15 hr | -20 °C | 60 J620 °C | 15 hr | -30 °C | EN 80Ar/20CO2? ?As welded100 J- | - | 20 °C | 73 J- | - | -40 °C | EN 80Ar/20CO2? ?Stress relieved130 J620 °C | 15 hr | 20 °C | 60 J620 °C | 15 hr | -20 °C | 60 J620 °C | 15 hr | -30 °C | Typical Tensile Properties<Tensile Strength | Elongation | Stress Relieved Temperature | Stress Relieved Testing Time | Yield Strength | AWS 80Ar/20CO2? ?As welded760 MPa- | - | - | - | EN 80Ar/20CO2? ?Stress relieved750 MPa20 % | 620 °C | 15 hr | 690 MPa | EN 80Ar/20CO2? ?As welded800 MPa19 % | - | - | 730 MPa | EN 80Ar/20CO2? ?Stress relieved750 MPa20 % | 620 °C | 15 hr | 690 MPa | EN 80Ar/20CO2? ?As welded800 MPa19 % | - | - | 730 MPa | EN 80Ar/20CO2? ?Stress relieved750 MPa20 % | 620 °C | 15 hr | 690 MPa | EN 80Ar/20CO2? ?As welded800 MPa19 % | - | - | 730 MPa | EN 80Ar/20CO2? ?Stress relieved750 MPa20 % | 620 °C | 15 hr | 690 MPa | 熔敷數據<安培 | 熔敷率 | 電壓 V | 直徑 | 送絲速度 | 80-280 A1-5,4 kg/h | 18-28 V | METRIC_0.8 mm | IMPERIAL_2,7-14,7 m/min | 80-280 A1-5,4 kg/h | 18-28 V | METRIC_0.9 mm | IMPERIAL_2,7-14,7 m/min | 80-280 A1-5,4 kg/h | 18-28 V | METRIC_1.0 mm | IMPERIAL_2,7-14,7 m/min | 120-350 A1,5-6,6 kg/h | 20-33 V | METRIC_1.2 mm | IMPERIAL_2,7-12,4 m/min | 225-480 A3,3-0 kg/h | 26-38 V | METRIC_1.6 mm | IMPERIAL_3,1-8,1 m/min |
中國焊接網
公眾號
在線客服